Matte parte tractata humilis profiles advolvit aeris ffoyle nigrum et rubrum color
Tractata humilis profiles advolvit aeris ffoyle cum nigrum / rufus matte latus
Advolvit aeris ffoyle characterem
During the downstream heating process, the material will undergo annealing changes at a temperature of 145°C within half an hour, The tensile strength and hardness of the material are reduced, and so the elongation is greatly increased, which provides sufficient elongation for the later bending and stretching of the flexible LED, The finished LED is not easy to break during the stretching and bending process.
●Et tractata advolvit aeris ffoyle cum matte latus
●Et tractata advolvit aeris ffoyle cum nigro matte latus
●Crassitudo, 9um 12um 18um 22um 35um 50um 70um
●Width, CCL ~ 630mm, vexillum width, 520mm, potest esse cutting ut petitionem
●Lignea buxum sarcina
●Quod productum est usque ad Rads environmental Signa
●ID: LXXVI mm
●Longitudo, customized
●Sample potest suppleret Support
●Volvuntur longitudinem core longitudinem, ut per petitionem
●Volvunt interiorem diameter et exterius diameter, ut petitionem
●Humilis asperitas
●Altum flexibilitate
●Effectus optimum etching
●Et tractata ffoyle in nigro vel rubrum
●Et nigrentur ffoyle habet alta flexibilitate, humilis superficiem asperitas et bonum physica et eget proprietatibus.
●Applicare ad FPC (flexuosi typis circuitu), utuntur agri: informatization et intelligentization; Altior-finis uber agro ut aerospace, medicinae apparatu et instrumentis, robots, communicationis ratio, computers et automotive electronics.
●Applicare ad FCCL / flexibilia aeris vestco laminam
●Applicare ad flexibilitate ducitur, summus finis flexibile ducitur et flexibile mobile telephono circuita tabulas et alium finem agros
●Flexibile typis circuitu
| Pario | Unitas | Test modus | ||||||||||||||
| Crassitudo nomina | Um | 9 | 12 | 18um | 35um | 22um | 50um | 70um | Test modus | |||||||
| Area pondus | G / M² | LXXX ± II | CVII ± III | CLX ± IV | CCCXI ± V | CXCVI ± IV | CDXLV ± V | DCXXIII ± V | GB / T29847-2013 | |||||||
| Pudicitia | % | Min.99.97 | GB / T5121 | |||||||||||||
| AGRESSUS | Crus parte (Ra) | Um | Max.0.2 | GB / T29847-2013 | ||||||||||||
| Matte latus (RZ) | Um | 0.8-1.2 | ||||||||||||||
| Tensile vires | Rm normalis | N / mm² | ≥370 | ≥370 | ≥370 | ≥370 | ≥370 | ≥370 | ≥370 | GB / T29847-2013 | ||||||
|
|
|
|
|
| ||||||||||||
| RM CLXXX ° C 30min. | ≥160 | ≥160 | ≥160 | ≥170 | ≥170 | ≥170 | ≥170 | |||||||||
| Elongatio | Normalis | % | ≥1.0 | ≥1.0 | ≥1.0 | ≥1.0 | ≥1.0 | ≥1.0 | 1It1.0 | GB / T29847-2013 | ||||||
| CLXXX ° C * 30min | ≥7 | ≥7 | ≥8 | ≥11 | ≥9 | ≥13 | ≥20 | |||||||||
| Cortices fortitudinem | N / mm | ≥0.8 | ≥0.8 | ≥1.0 | ≥1.2 | ≥1.0 | ≥1.4 | ≥2.0 | GB / T29847-2013 | |||||||
| Superficiem species | / | Uniformis color:Non rugam,Nulla scratche,Nemo pit et salientem illud | ||||||||||||||
| Chemical resistentia | % | Max.5 | ||||||||||||||
| Oxidatio resistentia | CC ° F / 60min | DECORDINATIO | Q / TBJB004-2015 | |||||||||||||
| Solder resistentiam |
| CCC ° F / 20s non pusterae | ||||||||||||||
Quod productum est usque ad Rads environmental vexillum.
Tractata humilis profiles advolvit aeris ffoyle cum Poetat / Rubrum Iamege